Products

DESCRIPTION

Basic Info.

Water Absorption	0.1%~0.3%
Tensile Strength	81~130MPa
Thickness	1.8mm-300mm
Density	1.2kg/Cm3
Light Transmission	93%
Certification	SGS/RoHS/CE
Resistant	Excellent Resistance to Weather
Surface	High Surface Hardness & Glossy
Transport Package	Cartons, Iron Pallet, PE Film, Kraft Paper
Specification	1220*2440,1220*1830,2050*3050,2000*3000/Customized
Trademark	Grandview
Origin	Guangdong
HS Code	3920510000
Production Capacity	10000 Tons/Year

Product Description

Products and Applications

Why Choose Us

3D design
1.Offer on site installation service and technical support
2.We serve customer with customized acrylic and turnkey project. In a word just tell us your dimension or suggestion; We will try.Our best to satisfy you. You can rest assured that both our quality and service are the best.
HOW TO ORDER

Products Description DATA SHEET Feature:
1.Warranty 20 years. 2.Outdoor use non-yellowing . 3.Lucite new material with 100% pureness. 4.100% Bonding No Bubble,the connector/gap non yellowing.

Material	Lucite Acrylic
Thickness	20-300mm customized
Color	Clear/transparent
Shape	Customer's Demand
Surface	High Surface Hardness
Light transmission	High light transmission(95%)
Diaphaneity	More than 93%
Packing	PE film masking on both sides,KT board and angle iron.
Application	undersea world, Oceanarium, Zoo, Luxurious hotels, Swimming pools and so on.

PROPERTIES	VALUES	RULES
Density	1.19 g/cm3	ISO 1183-1:2012 Method A
Rockwell Hardness	112L	ISO 2039-2:1999
Tensile Modulus	3150MPa	EN ISO 527:2012
Tensile Strength	80.0MPa	EN ISO 527:2012
Tensile Strain at Break	3.2%	EN ISO 527-1:2012
Water Absorption	0.20%	ISO 62:2008 Method 1
Total Luminous Transmittance	93.4%	ISO 13468-1:1996
Vicat Softening Temperature	105ºC	ISO 306:2013 Method B50
Light Ageing Test- UV Exposure	Grey scale: 5	ISO 4892-3:2016 Cycle 1
Mean Coefficient of Linear Thermal Expansion	72×10-6 K-1	ISO 11359-1:2014
Compressive Stress at Yield	129MPa	EN ISO 604:2003
Flexural Strength	120MPa	ISO 178:2013
Compressive Yield Strength	111MPa	ASTM D695-15
Compressive Modulus	3450MPa	ASTM D695-15
Shear Strength	59.7MPa	ASTM D732-17
Deflection Temperature under Load	100.2ºC	ASTM D648-18 Method B
Modulus Elasticity	2810MPa	ASTM D695-15

5.Maximum 300mm can be one time cast without laminated. 6.Heating again in Anneal Oven, Eliminate Environmental Stress. 7.numerical control center mold, more precise for bending size. 8.exist environment in -40ºC to 80ºC. Packaging and shippingCertifications and company